Product details
Minimum Order Quantity | 200 Kg |
Coefficient of thermal expansionat Degree C | 20-700 Deg C |
Cooling | Furnace |
Hardening Degree C | 1040-1060 Deg C |
Hardness after quenching HRC | 52 HRC |
Hardness HB | Max 185 |
Quenching | Oil or Hot Bath 500-550 Degree C |
Soft annealing Degree C | 740 - 800 Deg C |
Surface Finish | Galvanized |
Shape | Round |
Material | Spring Steel |
Diameter | 71 - 300 mm |
Single Piece Length | 3 - 18 Meter |
Usage/Application | Construction |
Chemical Composition - (Typical Analysis in %)
STANDARDS | X210CrW12 | H10 | DIN 2365 | AISI H10 | AFNOR 32CDV12-28 |
C | Si | Mn | P | S | Cr | Mo | V |
0.28-0.35 | 0.10-0.400000 | 0.20-0.40 | 0.003 max | 0.030max | 2.70-3.20 | 2.50-3.00 | 0.40-0.75 |
USA | Germany | Japan | British |
AISI / SAE | DIN, WNr | JIS G4404 | BS 4659 |
H10 / T20810 | 1.2365 / 32CrMoV12-28 | SKD7 | BH10 |
Physical Properties:
Coefficient of Thermal Expansion at °C | 10¯??? m / (m*K) |
20-100 | 11.7 |
20-200 | 12.4 |
20-300 | 12.7 |
20-400 | 13.2 |
20-500 | 13.5 |
20-600 | 13.7 |
20-700 | 13.8 |
Thermal Conductivity at °C | W / (m*K) |
20 | 32.6 |
350 | 34.4 |
700 | 32.4 |
Heat Treatment
Soft Annealing °C | 740-800 |
Cooling | Furnace |
Hardness HB | max. 185 |
Hardening °C | 1040-1060 |
Quenching | Oil or Hot Bath 500-550°C |
Hardness after quenching HRC | 52 |
Tempering°C after quenching | 100 | 210 | 300 | 400 | 500 | 550 | 600 | 650 | 700 |
HRC | 51 | 50.5 | 50 | 50 | 53 | 51 | 48 | 41 | 34 |